L605 Uns Light Rod Plate High Temperature Alloy ASTM

Brand Name : KAIXIN

Model Number : KX-Alloy605

Certification : ISO9001:2015

Place of Origin : China

MOQ : 200KG

Price : To negotiate

Payment Terms : T/T, L/C

Supply Ability : 50~80TONS per MONTH

Delivery Time : 45~60days

Packaging Details : Wooden Box, size as per guests request

Shape : Wire, Strip, Rod, Tube, Plate

Alloy Type : Nickel-based Deformed Superalloy

Raw Materials : NI9-11%,CR19-21%,W14-16%,MO Rem

Executive Standard : ASTM

Delivery State : Sosoloid

Application : Manufacture engine guide blade, turbine outer ring, outer wall, swirler, sealing plate and etc parts

Features : Excellent stability and high strength

Size : Negotiable

Contact Now

KX L605 Uns Light Rod Plate Structural Operating Temperature Range For High Temperature Alloy

Product Description and Application

GH605 is also known as L605,UNSR30605,GH5605

GH605 is a Co-Cr-Ni based solid solution enhanced deformation superalloy, its use temperature is below 1000℃. Cobalt-based superalloy GH605 is a cobalt base alloy strengthened by solution of 20%Cr and 15%W(percent mass). It has medium durability and creep strength below 815℃, excellent oxidation resistance below 1 090℃, and satisfactory process properties such as forming and welding. It is a key material for aero engine, rocket engine, naval ship and industrial gas turbine. Its development and production status is one of the symbols on the metal materials development level in a country. It is used for manufacturing the high temperature parts of aero engine guide blade, turbine outer ring, outer wall, swirler and sealing plate.

Process Performance and Requirements

  • Product Fusion Process

Vacuum Induction Furnace(VIM) and Electroslag Remelting Furnace(ESR)

  • Product Chemical Composition

Composition Fe C Si Mn P S Cr Ni W More
Min - 0.05 - 1 - - 19 9 14 Co:Rem
Max 3 0.15 0.4 2 0.04 0.03 21 11 16

  • Product Physical Property

Density p=9.13g/cm3
Melting Temperature Range 1330℃-1410℃

  • Product Mechanical Property

Variety Tensile Property in the Room Temperature

Hardness

HV

 815℃ Durability Grain Size/Grade Other properties
MPa MPa MPa MPa t/h %
Middle Plate,Sheet,Strip ≧890 370-550 ≧35 ≤290 165 ≧24 ≧10 ≧2.5(1) Bend

Cold Hard Strip

Grade A

 ≧1500 ≧1300 ≧5 410-480 --- ---- --- ≧9 Bend

Cold Hard Strip

Grade B

 ≧1700 ≧1500 ≧3 485-560 --- --- --- ≧10 Bend
Bar ≧860 ≧340 ≧35 ≤ 282 165 ≧ 23 ≧10 ≧2(0) ---
Ring ≧860 ≧310 ≧30 ≤ 248 165 ≧ 24 ≧10 ≧2(0) ---

  • Productive Process

L605 Uns Light Rod Plate High Temperature Alloy ASTM

  • Professional Customization

Cold-drawn Wire ¢0.3~¢18mm(Delivery in rolls or trays)
Hot-Rolling Wire ¢5.5~¢20mm(Delivery in rolls)
Strip thickness 0.1~4.5*width 6~350mm(Supply in rolls or straight strips)
Smooth Forged Rod on a Lathe

¢60~350mm,L800-2500mm
Hot-rolled Burnishing ¢20~80mm,L1000-5000mm
Cold Drawn and Burnishing ¢2.5~18mm,L1000-8000mm
Seamless Tube ¢1~275mm,wall thickness 0.2~30,L1000-8000mm

L605 Uns Light Rod Plate High Temperature Alloy ASTM

L605 Uns Light Rod Plate High Temperature Alloy ASTML605 Uns Light Rod Plate High Temperature Alloy ASTML605 Uns Light Rod Plate High Temperature Alloy ASTML605 Uns Light Rod Plate High Temperature Alloy ASTM


Product Tags:

L605 High Temperature Alloy

      

Uns High Temperature Alloy

      

ASTM high resistance alloy

      
L605 Uns Light Rod Plate High Temperature Alloy ASTM Manufactures

L605 Uns Light Rod Plate High Temperature Alloy ASTM Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Danyang Kaixin Alloy Material Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like